Canlon Fiber-Reinforced Tpo Waterproof Membrane Professional Building Materials Roofing Membrane

Product Description

Product Description

Crafted from cutting-edge thermoplastic polyolefin (TPO) material, Jiangsu Canlon Building Materials Co., Ltd. masterfully merges the weldability of propylene-alpha-olefin copolymer resins produced through state-of-the-art polymerization processes, enhanced with the robust durability of polypropylene resins. The innovative Canlon TPO-L stands as an advanced composite thermoplastic polyolefin polymer waterproofing membrane, elegantly reinforced with non-woven fleece backing via pioneering processing technology, ideal for fully adhered roofing systems.

Detailed Photos

Application

• Industrial Plants: automobiles, electronics, machinery, *** factories, and more...

• Transportation Hubs: airport terminals, high-speed railway stations, passenger terminals, and more...

• Public Buildings: convention and exhibition centers, exhibition halls, stadiums, and more...

• New Infrastructure: big data centers, logistics centers, and more...

Product Features

• Outstanding long-term UV resistance;

• Superior weldability;

• Remarkable low-temperature flexibility;

• Exceptional dimensional stability;

• Excellent elongation properties;

• Impressive impact resistance;

• High solar reflectivity;

• Energy-efficient and environmentally friendly, fully recyclable.

Colors

Surface: White

Backside: White

Specifications

Each standard roll is carefully encapsulated in polyethylene film. The width is 2.0m, with length varying by membrane thickness.

0.8mm: 30m (Approx. 48-50kg per roll)

1.2mm: 25m (Approx. 55-57kg per roll)

1.5mm: 20m (Approx. 67-69kg per roll)

1.8mm: 15m (Approx. 60-62kg per roll)

2.0mm: 15m (Approx. 66-68kg per roll)

Installation Instructions

Technical Data Sheet

 

NO.	Item		Value
			Smooth one (Category H)	Fiber fleece-backed (Category L)	Reinforced with polyester scrim (Category P)
1	Thickness of resin attaching to embedded scrim/ mm  ≥		----------	----------	0.4
2	Tensile property	Max tensile force / N/cm                            ≥	----------	120	250
		Tensile strength/ MPa                               ≥	12.0	----------	----------
		Elongation at break/ %                              ≥	500	250	---------
3	Dimensional variation after heating/  100%                  ≤		2.0	1.0	0.5
4	Low temperature flexibility		-40ºC (no crack)
5	Impermeability		0.3MPa, 2h , impermeable
6	Compression resistance		0.5kg.m (no penetration)
7	Tear strength of overlapping  /  N/mm                          ≥		4.0	3.0
8	Water absorption (70 ºC  168h) / %                              ≤		4.0
9	Heat aging (80ºC)	Time duration	672h
		Appearance	No bubble, crack, delamination, or pinhole
		Retention rate of max tensile force / %     ≥	----------	90	90
		Retention rate of tensile strength /  %       ≥	90	----------	----------
		Retention rate of elongation at break/ %   ≥	90	90	----------
		Low-temperature flexibility	-40ºC (no crack)
10	Chemical resistance	Appearance	No bubble, crack,  delamination, or pinhole
		Retention rate of max tensile force / %     ≥	----------	90	90
		Retention rate of tensile strength/ %         ≥	90	----------	----------
		Retention rate of elongation at break/ %   ≥	90	90	----------
		Low temperature flexibility	-40ºC (no crack)
11	Artificial Weathering	Time duration	1500h^b)
		Appearance	No bubble, crack,  delamination, or pinhole
		Retention rate of max tensile force / %     ≥	----------	90	90
		Retention rate of tensile strength /  %       ≥	90	----------	----------
		Retention rate of elongation at break /      ≥	90	90	----------
		Low temperature flexibility	-40ºC (no crack)