CL-PMC
CL-PMC is a two components water-based waterproof coating. Component A is consisted of high quality modified acrylic emulsion and various additives. Component B is consisted of iron-rich containing and high-alumina cement. It has the outstanding acrylic ester polymer emulsion-based performance and forms membranes with high elongation rate (above 200%), weather resistance for non-permanent immersion environment.
Where to use
Bathroom, kitchen, floors and balcony;
Waterproof layers;
Waterproof constructions under non-permanent immersion environment.
Advantages
Water-based environmental-friendly coatings;
High tensile strength with water resistance and weather resistance;
Can be applied on wet substrates with tight bonding;
Cold and convenient to apply;
Waterproofing functions with impermeableness and moisture proofing.
| Item |
Requirement |
| Solid content, % ≥ |
70 |
| Tensile strength, MPa ≥ |
No treatment, MPa ≥ |
1.2 |
| Retention rate after heat treatment, % ≥ |
80 |
| Retention rate after akali treatment, % ≥ |
60 |
| Retention rate after water immersion, % ≥ |
60 |
| Retention rate after UV treatment, % ≥ |
80 |
| Elongation at break, % ≥ |
No treatment, MPa ≥ |
200 |
| Heat treatment, % ≥ |
150 |
| Alkali treatment, % ≥ |
150 |
| Water immersed treatment, % ≥ |
150 |
| UV treatment, % ≥ |
150 |
| Flexibility at low temperature, ° C |
-10° C, no cracks |
| Boding strength |
No treatment, MPa ≥ |
0.5 |
| Wet substrate, MPa ≥ |
0.5 |
| Alkali treatment, MPa ≥ |
0.5 |
| Water immersed treatment, MPa ≥ |
0.5 |
| Water tightness, 0.3MPa, 30min |
Pass |