Customization: | Available |
---|---|
Certification: | CE, ISO, MSDS |
Color: | Grey |
Still deciding? Get samples of US$ 0/Piece
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Crafted from cutting-edge thermoplastic polyolefin (TPO) material, this exceptional membrane combines the superior weldability of propylene-alpha-olefin copolymer resins-sourced from advanced polymerization processes-with the enduring strength of polypropylene resins. Canlon TPO-L stands as a composite thermoplastic polyolefin polymer waterproofing solution fortified with a non-woven fleece backing, produced through state-of-the-art processing technology. It is designed specifically for fully adhered roofing systems.
Each standard roll is carefully encapsulated in polyethylene film. The width is 2.0m, with lengths varying according to membrane thickness.
NO. | Item | Value | |||
Smooth one (Category H) |
Fiber fleece-backed (Category L) |
Reinforced with polyester scrim (Category P) | |||
1 | Thickness of resin attaching to embedded scrim/ mm ≥ | ---------- | ---------- | 0.4 | |
2 | Tensile property | Max tensile force / N/cm ≥ | ---------- | 120 | 250 |
Tensile strength/ MPa ≥ | 12.0 | ---------- | ---------- | ||
Elongation at break/ % ≥ | 500 | 250 | --------- | ||
3 | Dimensional variation after heating/ 100% ≤ | 2.0 | 1.0 | 0.5 | |
4 | Low temperature flexibility | -40ºC (no crack) | |||
5 | Impermeability | 0.3MPa, 2h , impermeable | |||
6 | Compression resistance | 0.5kg.m (no penetration) | |||
7 | Tear strength of overlapping / N/mm ≥ | 4.0 | 3.0 | ||
8 | Water absorption (70 ºC 168h) / % ≤ | 4.0 | |||
9 | Heat aging (80ºC) |
Time duration | 672h | ||
Appearance | No bubble, crack, delamination, or pinhole | ||||
Retention rate of max tensile force / % ≥ | ---------- | 90 | 90 | ||
Retention rate of tensile strength / % ≥ | 90 | ---------- | ---------- | ||
Retention rate of elongation at break/ % ≥ | 90 | 90 | ---------- | ||
Low-temperature flexibility | -40ºC (no crack) | ||||
10 | Chemical resistance |
Appearance | No bubble, crack, delamination, or pinhole | ||
Retention rate of max tensile force / % ≥ | ---------- | 90 | 90 | ||
Retention rate of tensile strength/ % ≥ | 90 | ---------- | ---------- | ||
Retention rate of elongation at break/ % ≥ | 90 | 90 | ---------- | ||
Low temperature flexibility | -40ºC (no crack) | ||||
11 | Artificial Weathering |
Time duration | 1500hb) | ||
Appearance | No bubble, crack, delamination, or pinhole | ||||
Retention rate of max tensile force / % ≥ | ---------- | 90 | 90 | ||
Retention rate of tensile strength / % ≥ | 90 | ---------- | ---------- | ||
Retention rate of elongation at break / ≥ | 90 | 90 | ---------- | ||
Low temperature flexibility | -40ºC (no crack) |